PAHT-CF Bambu Lab

120.000 JD

Bambu PAHT-CF Bambu PAHT-CF is a composite material made from PA12 and carbon fiber. It combines the low water absorption properties of PA12 with the high-performance characteristics of carbon fiber. As a result, Bambu PAHT-CF exhibits excellent mechanical and thermal properties that are well-preserved even when the prints become wet....

Categories : Fiber Reinforced, Filaments, PA/PAHT

Description
Review

Bambu PAHT-CF

Bambu PAHT-CF is a composite material made from PA12 and carbon fiber. It combines the low water absorption properties of PA12 with the high-performance characteristics of carbon fiber. As a result, Bambu PAHT-CF exhibits excellent mechanical and thermal properties that are well-preserved even when the prints become wet. Its higher Z-axis adhesion and flexibility make it an ideal choice for creating engineering components, such as functional prototypes, machining fixtures, injection molds, jigs, and low-volume production parts.

Low water absorption

Bambu PAHT-CF has a 50% lower water absorption rate compared to standard PA-CF, ensuring excellent mechanical properties and dimensional stability even in high humidity conditions.

Deflection from Dry to Wet

Mechanical Properties Comparison

	Normal PA-CF	PAHT-CF
Saturated Water Absorption Rate/% ( 25 °C, 55% RH )	1.70	0.88
Bending Strength - XY/MPa (Dry)	128	125
Bending Strength - XY/MPa (Wet)	76	115
Bending Strength - Z/MPa (Dry)	48	61
Bending Strength - Z/MPa (Wet)	34	49
Bending Modulus - XY/MPa (Dry)	4420	4230
Bending Modulus - XY/MPa (Wet)	2210	3640
Bending Modulus - Z/MPa (Dry)	1470	1820
Bending Modulus - Z/MPa (Wet)	770	1480
Decline rate of mechanical properties after absorbing water/%	40%-45%	12%-18%

*Both PA-CF and PAHT-CF need to be dried at 80 °C for 12 hours before printing.

Exceptional Z-bonding

Bambu PAHT-CF shows much higher adhesion in Z layers compared to normal PA-CF,

bringing it the ability to withstand high levels of impact or stress without breaking or deforming.

Z-layer Performance

	Normal PA-CF	PAHT-CF	Improved %
Bending Strength - Z/MPa	48	61	27%
Bending Modulus - Z/MPa	1470	1820	24%
Impact Strength - Z/(kJ/m²)	5.7	13.3	133%

*Both PA-CF and PAHT-CF need to be dried at 80 °C for 12 hours before printing.

High tensile strength

Bambu PAHT-CF is designed to meet the demands of various industrial

and engineering applications where high strength and durability are required.

Designed for high-temperature resistance

The heat deflection temperature of Bambu PAHT-CF is up to 194℃ (0.45MPa)*, making it useful in applications where the printed parts may be exposed to high temperatures without deforming or losing their strength.

*The long-term temperature resistance is related to the structure and usage scenario of the model itself.

Reusable spool

Bambu PAHT-CF comes with a high-temperature resistant spool, which is not prone to deformation in the drying process. Continuing our concept of reducing plastic waste, the spool can also be reused with other Bambu refills.

Accessory Compatibility

	Recommended	Not Recommended
Build Plate	Smooth PEI Plate, Textured PEI Plate	Cool Plate SuperTack
Hotend	Hotend with Hardened Steel 0.4mm / 0.6mm (recommended) / 0.8 mm	Hotend with Stainless Steel Nozzle All Size
Glue	Glue Stick	Liquid Glue

*As the nozzle size increases, the probability of clogging decreases, but the print quality also decreases. Therefore, it is recommended to use a 0.6 mm Hardened Steel nozzle to avoid clogging while maintaining optimal print quality.

RFID for Intelligent Printing

All printing parameters are embedded in RFID, which can be read through our AMS (Automatic Material System).

Load and print! No more tedious setting steps.

Parameters Comparison

Learn more different filaments comparison on Bambu Filament Guide >>

	PET-CF	PAHT-CF
Composition	PET, carbon fiber	PA 12 and other long-chain PA, carbon fiber
Hotend Compatibility	Hardened Steel 0.6 (recommended), 0.4, 0.8 mm
Build Plate Compatibility	Engineering Plate, High Temperature Plate, Textured PEI Plate
Glue	Glue Stick / Liquid Glue	Glue Stick
AMS Compatibility	NO	YES
Print Speed	< 100 mm/s	< 100 mm/s
Toughness (Impact Strength - XY)	36.0 kJ/m²	57.5 kJ/m²
Strength (Bending Strength - XY)	131 MPa	125 MPa
Stiffness (Bending Modulus - XY)	5320 MPa	4230 MPa
Layer Adhesion (Impact Strength - Z)	4.5 kJ/m²	13.3 kJ/m²
Heat Resistant（HDT, 0.45 MPa）	205 °C	194 °C
Saturated Water Absorption Rate / % (25 °C，55% RH)	0.37	0.88

Recommended Printing Settings
Drying Settings (Blast Drying Oven)	80 °C, 8 - 12 h
Printing and Keeping Container's Humidity	< 20% RH (Sealed, with Desiccant)
Nozzle Temperature	260 - 290 °C
Bed Temperature (with Glue)	80 - 100 °C
Printing Speed	< 100 mm/s

Physical Properties
Density	1.06 g/cm³
Vicat Softening Temperature	220 °C
Heat Deflection Temperature	194 °C
Melting Temperature	225 °C
Melt Index	14.4 ± 2.0 g/10 min

Mechanical Properties
Tensile Strength	92 ± 7 MPa
Breaking Elongation Rate	8.4 ± 1.8 %
Bending Modulus	4230 ± 210 MPa
Bending Strength	125 ± 7 MPa
Impact Strength	57.5 ± 3.4 kJ/m²

Downloads

Filament TDS

Filament MSDS

Filament RoHS

Printing Tips

•Drying conditions: 80℃ for 8 hrs. PAHT-CF is highly sensitive to humidity. To achieve optimal printing performance, it is recommeded further drying before use and after storage. For more details please refer to: Filament drying instructions on WIKI.

• Bambu PAHT-CF has high thermal insulation requirements during the printing process, making it unsuitable for use with open-frame printers.

• When printing a model with support, we recommend removing the support structures within 2 hours after printing to prevent them from sticking after absorbing moisture. If sticking occurs, dry the model to ease the removal.

• For better print results, please refer to: Printing tips for Engineering materials on WIKI.

What's in the Box

Filament with Spool*1 & Desiccant*1

Package*1

*Test Conditions

Specimen Size	150 mm (L) * 10 mm (W) * 2.5 mm (H)
Loading Weight	1.02 KG
Printing Settings	All specimens were printed at a nozzle temperature of 280℃, bed temperature of 100℃, and printing speed of 100mm/s.
Filament States	•Dry specimens were annealed and dried at 80°C for 12 hours before testing. • Wet specimens were placed under the environment conditions of 25℃, 55% RH and reached the saturated water absorption rate.